Home > Gaskets & Pads Function > Low Temperature Gaskets

Low Temperature Gaskets and Low Temp Cushion Pads

Stockwell Elastomerics manufactures custom low temp gaskets and cushioning pads from various gasket materials to customer specification.

Elastomeric gaskets and cushioning pads can be relatively sensitive to low temperatures. Temperatures listed on material datasheets don't always translate into functional temperatures in an application. Low temperature testing for elastomeric gasket materials is usually limited to brittleness or cracking test. Expanded rubber products such as sponges and foams are usually tested under ASTM D 1056, solid elastomers are often tested under ASTM D 2137 (brittleness test).

Low Temp Test - ASTM D 1056 - Cellular Material

Cold soak for 5 hours at the appropriate temperatures (per suffix shown below) and bend 180° around a mandrel. Inspect samples for any cracking and see if it is still pliable; no signs of cracking are allowed. If the material is not pliable or cracks, it's considered unsuitable for applications at or below the test condition.

  • Suffix F1: - 40°C (-40°F)
  • Suffix F2: - 55°C (-67°F)
  • Suffix F3: - 75°C (-103°F)

Rubber Low Temperature vs. Functional Low Temp

Cold flex tests offer the low temperature of material however in real world applications this typically doesn't translate to a functional low temperature. This is very apparent with cushioning pad applications.

Example: Cushioning Pad, Handheld Device Cold Drop Test Ruggedized mobile device is cold soaked at -20°C then dropped from 48" or 60" and must function properly after the drop test. Internal components are often protected by an external rubber shell and cushioning pads inside the device. Urethane is often used for ambient applications, however at low temperatures urethane turns hard, losing its dampening properties. Even moderately low temperatures are enough to harden foam to a point where energy from a drop is transferred to sensitive electronics.

PORON Compressive Forces
The curves above show a shift in compressive forces for a PORON® urethane foam that was cold soaked for 48hrs at 20°F. Click graph for larger chart.

Low Temperature Rubber Materials

As with all gasket and cushioning pad applications, environmental conditions should be considered in conjunction with the functional requirements of the device. Silicone is regularly specified for low temperature applications that require a gasket or pad to remain flexible and compliant. There are a wide range of silicone products to select from for specific applications such as; soft silicone sponges and foams, soft (low durometer) silicone sheets, custom molded solid silicone. Many of the commercially available silicone products are well suited for meeting MIL-STD-810 testing including low temperature, high temperature, UV resistance, salt fog and water sealing.

Contact Stockwell Elastomerics for Low Temperature Gasket Materials and Low Temperature Cushion Pads

Contact Us for further assistance with custom low temp gaskets and low temp gasket material.